The key to success.
Manufacturing its own spare parts and not depending on external suppliers is the key to Canela's success, which even has its own investment casting where all the flanges, levers and all the cast elements that a tool may need are manufactured.
duplication text
| MATERIAL | CHEMICAL ANALYSIS | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| DIN | UNI | %C | %Si | %Mn | %P | %S | %Cr | %Mo | %Ni | %Cu | %V | %W | |
| LOW ALLOYED STEELS | 1.7220 | F1252 | 0,34 0,40 | 0,10 0,40 | 0,60 0,90 | – 0,035 | – 0,035 | 0,80 1,10 | 0,15 0,25 | – – | – – | – – | – – |
| 1.6511 | F1280 | 0,30 0,40 | 0,10 0,35 | 0,35 0,85 | – 0,04 | – 0,04 | 0,80 1,20 | 0,30 0,40 | 0,80 1,20 | – – | – – | – – | |
| 1.3505 | F1310 | 0,95 1,20 | 0,10 0,35 | 0,20 0,40 | – 0,04 | – 0,04 | 1,40 1,80 | – – | – – | – – | – – | – – | |
| 1.8159 | F1430 | 0,47 0,54 | 0,15 0,40 | 0,70 1,00 | – 0,035 | – 0,035 | 0,90 1,20 | – – | – – | – – | 0,10 0,20 | – – | |
| 1.5810 | F1580 | 0,17 0,22 | 0,15 0,40 | 0,70 1,00 | – 0,035 | – 0,035 | 0,80 1,20 | – – | 0,80 1,20 | – – | – – | – – | |
| 1.2842 | 90MnCrV8 | 0,85 0,95 | 0,10 0,40 | 1,70 2,20 | – 0,03 | – 0,03 | 0,20 0,50 | – – | – – | – – | 0,10 0,30 | – – | |
| 1.3401 | X120Mn18 | 1,10 1,30 | 0,30 0,50 | 12,0 13,0 | – 0,10 | – 0,10 | – 1,50 | – – | – – | – – | – – | – – | |
| 1.7218 | 25CrMo4 | 0,22 0,29 | 0,15 0,40 | 0,60 0,90 | – 0,035 | – 0,035 | 0,90 1,20 | 0,15 0,30 | – – | – – | – – | – – | |
| 1.7225 | 42CrMo4 | 0,38 0,45 | 0,10 0,40 | 0,60 0,90 | – 0,035 | – 0,035 | 0,90 1,20 | 0,15 0,30 | – – | – – | – – | – – | |
| 1.7228 | 50CrMo40 | 0,46 0,54 | 0,25 0,30 | 0,30 0,80 | – 0,035 | – 0,035 | 0,90 1,20 | 0,15 0,25 | – – | – – | – – | – – | |
| MEDIUM ALLOYED STEELS | 1.8519 | F1721 | 0,28 0,35 | 0,15 0,40 | 0,50 0,70 | – 0,035 | – 0,035 | – – | – – | 0,20 0,30 | – – | ||
| 1.2344 | F5318 | 0,35 0,45 | 0,90 1,20 | 0,25 0,55 | – 0,035 | – 0,035 | – – | – – | 0,85 1,15 | – – | |||
| 1.7380 | A217 WC9 | 0,05 0,18 | 0,10 0,60 | 0,40 0,70 | – 0,040 | – 0,040 | 0,10 0,50 | 0,10 0,50 | – – | – 0,10 | |||
| 25CrM012 | F1711 | 0,22 0,29 | 0,15 0,40 | 0,40 0,70 | – 0,035 | – 0,035 | – – | – – | – – | – – | |||
| HIGH ALLOYED STEELS | 1.4021 | F3402 | 0,17 0,23 | 0,10 1,00 | 0,10 1,00 | – 0,040 | – 0,030 | – 0,10 | – – | – – | – – | ||
| 1.2080 | F5212 | 1,90 2,20 | 0,10 0,40 | 0,15 0,45 | – 0,030 | – 0,030 | – – | – – | – – | – – | |||
| 1.2510 | F5220 | 0,90 1,05 | 0,10 0,40 | 1,05 0,35 | – 0,030 | – 0,030 | – – | – – | 0,05 0,25 | 0,40 0,70 | |||
| 1.4031 | AISI 420 | 0,37 0,40 | 0,50 1,00 | 0,50 1,00 | – 0,040 | – 0,030 | – – | – – | – – | – – | |||
| 1.4008 | 6X7CrNi Mo12-21 | 0,06 0,12 | 0,10 1,00 | 0,10 1,00 | – 0,045 | – 0,030 | 1,60 2,00 | – – | – – | – – | |||
| 1.4112 | X90CrMo V18 | 0,85 0,95 | 0,10 1,00 | 0,10 1,00 | – 0,040 | – 0,020 | – – | – – | 0,07 0,12 | – – | |||
| 1.4931 | 6X23CrMo V12-1 | 0,20 0,26 | 0,10 0,40 | 0,50 0,80 | – 0,030 | – 0,020 | 0,10 1,00 | – – | 0,25 0,35 | 0,05 0,50 | |||
| CARBON STEELS | 1.0401 | F1110 | 0,10 0,20 | 0,15 0,30 | 0,30 0,50 | – 0,040 | – 0,040 | – – | – – | – – | – – | – – | – – |
| 1.0402 | F1120 | 0,20 0,30 | 0,15 0,30 | 0,40 0,70 | – 0,040 | – 0,040 | – – | – – | – – | – – | – – | – – | |
| 1.0501 | F1130 | 0,30 0,40 | 0,15 0,30 | 0,40 0,70 | – 0,040 | – 0,040 | – – | – – | – – | – – | – – | – – | |
| 1.0503 | F1140 | 0,40 0,50 | 0,15 0,30 | 0,40 0,70 | – 0,040 | – 0,040 | – – | – – | – – | – – | – – | – – | |
| 1.0535 | F1150 | 0,50 0,60 | 0,15 0,30 | 0,40 0,70 | – 0,040 | – 0,040 | – – | – – | – – | – – | – – | – – | |
| 1.0420 | A27Gr6030 | 0,10 0,25 | 0,10 0,80 | 0,10 0,75 | – 0,040 | – 0,040 | – 0,10 | – 0,10 | – 0,10 | – – | – – | – – | |
| 1.0619 | A216WCB | 0,18 0,23 | 0,10 0,60 | 0,50 1,20 | – 0,030 | – 0,030 | – – | – – | – – | – – | – – | – – | |
| MATERIAL | CHEMICAL ANALYSIS | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| DIN | UNI | %C | %Si | %Mn | %P | %S | %Cr | %Mo | %Ni | %Others | ||
| STAINLESS STEELS | 1.4305 | AISI 303 | – 0,15 | 0,20 1,00 | 0,50 1,00 | – 0,200 | 0,150 0,350 | 17,0 19,0 | – 0,60 | 8,00 10,00 | – | |
| 1.4301 | AISI 304 | – 0,08 | 0,30 1,00 | 0,50 2,00 | – 0,045 | – 0,030 | 18,0 20,0 | – – | 8,00 10,50 | – | ||
| 1.4841 | AISI 310 | – 0,25 | 0,50 1,50 | 0,50 2,00 | – 0,045 | – 0,030 | 24,0 26,0 | – – | 19,0 22,0 | – | ||
| 1.4401 | AISI 316 | – 0,08 | 0,30 1,00 | 0,50 2,00 | – 0,045 | – 0,030 | 16,0 18,0 | 2,00 3,00 | 10,0 14,0 | – | ||
| 1.4571 | AISI 316Ti | – 0,08 | 0,80 1,00 | 0,50 2,00 | – 0,045 | – 0,030 | 16,0 18,0 | 2,00 3,00 | 10,0 14,0 | Ti 0,15 Ti 0,80 | ||
| 1.4057 | AISI 431 | – 0,20 | 0,50 1,00 | 0,50 1,00 | – 0,040 | – 0,030 | 15,0 17,0 | – – | 1,25 2,50 | – | ||
| 1.4823 | A297 HD | – 0,50 | 1,00 2,00 | 1,00 1,50 | – 0,040 | – 0,040 | 26,0 30,0 | 0,20 0,50 | 4,00 7,00 | – | ||
| 1.4006 | A217 CA15 | – 0,15 | 0,50 1,50 | 0,20 1,00 | – 0,040 | – 0,040 | 11,5 14,0 | – 0,50 | – 1,00 | – | ||
| 1.4833 | A351 CH8 | – 0,08 | – 1,50 | – 1,50 | – 0,040 | – 0,040 | 22,0 26,0 | – – | 12,0 15,0 | – | ||
| 1.4308 | CF-8 | – 0,07 | 0,50 1,50 | – 1,50 | – 0,040 | – 0,030 | 18,0 20,0 | – 0,50 | 8,00 11,0 | – | ||
| 1.4404 | AISI 316L | – 0,03 | 0,50 1,50 | 0,50 1,50 | – 0,035 | – 0,020 | 17,0 20,0 | 2,00 3,00 | 9,00 13,0 | – | ||
| 1.4408 | CF-8M | – 0,07 | 0,50 1,50 | 0,50 1,50 | – 0,040 | – 0,030 | 18,0 20,0 | 2,00 2,50 | 9,00 12,0 | – | ||
| 1.4435 | – | – 0,03 | 0,50 1,00 | 0,50 1,50 | – 0,045 | – 0,025 | 17,0 18,5 | 2,50 3,00 | 12,5 15,0 | – | ||
| 1.4462 | – | – 0,03 | 0,20 1,00 | 0,50 2,00 | – 0,030 | – 0,020 | 21,0 23,0 | 2,50 3,50 | 4,50 6,50 | N 0,08 N 0,20 | ||
| 1.4542 | – | – 0,07 | – 1,00 | – 1,00 | – 0,045 | – 0,030 | 15,0 17,.0 | – – | 3,00 5,00 | Nb 0,15 Nb 0,45 | ||
| 1.4548 | – | – 0,07 | 0,30 1,00 | 0,30 1,00 | – 0,025 | – 0,025 | 15,0 17.0 | – – | 3,00 5,00 | Nb 0,15 Nb 0,45 | ||
| 1.4552 | – | – 0,07 | 0,50 1,50 | 0,50 1,50 | – 0,040 | – 0,030 | 18,0 20,0 | – – | 9,00 12,0 | Nb 0,15 Nb 0,45 | ||
| 1.4581 | – | – 0,07 | 0,50 1,50 | 0,50 1,50 | – 0,040 | – 0,030 | 18,0 20,0 | 2,00 2,50 | 9,00 12,0 | Nb 0,40 Nb 0,60 | ||
| STAINLESS STEELS WITH CARBON | 1.4837 | A297 GrHH | 0,20 0,50 | 1,00 2,00 | 1,00 2,00 | – 0,040 | – 0,040 | 24,0 28,0 | – 0,50 | 11,0 14,0 | – | |
| 1.4848 | – | 0,30 0,50 | 1,00 2,50 | – 1,50 | – 0,035 | – 0,030 | 24,0 26,0 | – – | 19,0 21,0 | Ar – Ar 0,15 | Cu – Cu 0,15 | |
| 1.4852 | – | 0,35 0,45 | 1,00 2,50 | 0,50 1,50 | – 0,035 | – 0,030 | 24,0 26,0 | – – | 33,0 35,0 | Nb 0,8 Nb 1,8 | ||
| MATERIAL | CHEMICAL ANALYSIS | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| %C | %Si | %Mn | %P | %S | %Cr | %Mo | %Ni | %Ar | %V | %W | %Others | ||||
| CHROME NICKEL ALLOYS | A560Gr 50Cr50Ni | – 0,100 | 0,30 1,00 | – 0,30 | – 0,020 | – 0,02 | 48,0 52,0 | – – | 50,0 51,0 | – 0,25 | – – | – – | N – N 0,3 | Ti – Ti 0,5 | Fe – Fe 1,0 |
| 60Cr 40Ni | – – | – – | – – | – – | – – | 59,5 60,0 | – – | 39,5 40,0 | – – | – – | – – | – – | |||
| HASTELLOY C 2.4686 | – 0,070 | 0,30 0,70 | 0,30 0,80 | – 0,040 | – 0,03 | 15,5 17,5 | 16,0 18,5 | 50,0 – | – – | 0,20 0,40 | 3,75 5,25 | Co – Co 1,25 | Fe 2,0 Fe 6,0 | ||
| HASTELLOY C22 2.4602 | – 0,015 | – 0,08 | – 0,50 | – 0,025 | – 0,01 | 20,0 22,5 | 12,5 14,5 | 50,0 – | – – | – 0,35 | 2,50 3,50 | Co – Co 2,50 | Fe 2,0 Fe 6,0 | ||
| 50Cr 50Ni Nb | – 0,100 | – 0,50 | – 0,30 | – 0,020 | – 0,02 | 47,0 52,0 | – – | – 0,25 | – 0,25 | – – | – – | Fe – Fe 1,10 | Nb 1,4 Nb 1,7 | Ti – Ti 0,5 | |
| MATERIAL | CHEMICAL ANALYSIS | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| %Cu | %Sn | %Pb | %Fe | %Mn | %Al | %Ni | %Zn | ||
| NON FERROUS MATERIALS | Latón L60/40Al Gk-Cu60Zm | 57,5 60,0 | – 1,20 | 1,50 3,00 | 0,30 0,80 | – 0,030 | 0,40 0,80 | 0,30 1,00 | Resta |
| Bronze Aluminium F60 | 76,0 82,5 | – 0,10 | – 0,03 | 4,00 5,30 | – 2,50 | 8,80 10,0 | 4,00 5,00 | – 0,40 | |
| Bronze RG10 | 88,5 90,5 | 9,30 11,0 | – 1,3 | – 0,15 | – – | – – | – 1,80 | – 0,50 | |
| Bronze R65 | 83,5 85,5 | 4,30 6,00 | 4,00 6,00 | – 0,02 | – – | – – | – – | 4,50 6,50 | |
| Aluminium | – 0,08 | – – | – – | – 0,08 | – – | – 10,0 | – – | – – | |
In order to restrain the production costs, it is a good norm to avoid adopting narrower tolerance fields than necessary for the real functional use of the parts.
Avoid adopting general indications of fixed and narrow fields for all the dimensions of a drawing; it is better to indicate the precision or quality degree of tolerance, referring to the dimensions where this is applied.
To sum up, the best tolerance field to be achieved with castings is of ±0,7 of the nominal value, with a minimum of ±0,10% mm for the dimensions lower than 15 mm.
On the enclosed table we have indicated the linear tolerances according to the precision degrees required. Please note that we will adopt the following degrees:
duplication
| NOMINAL DIMENSIONS | LENGHT, WIDTH, HEIGHT | BETWEEN AXES | |||||||
|---|---|---|---|---|---|---|---|---|---|
| PRECISION DEGREE | |||||||||
| D1 | D2 | D3 | D1 | D3 | |||||
| DA | A | Variation ±0- | Tolerance field | Variation ±0- | Tolerance field | Variation ±0- | Tolerance field | Variation ±0- | Variation ±0- |
| 6 | ±0,10 | 0,20 | ±0,08 | 0,16 | ±0,06 | 0,12 | ±0,25 | ±0,16 | |
| 6 | 10 | ±0,12 | 0,24 | ±0,10 | 0,20 | ||||
| 10 | 14 | ±0,15 | 0,30 | ±0,12 | 0,24 | ±0,09 | 0,18 | ||
| 14 | 18 | ±0,20 | 0,40 | ±0,14 | 0,28 | ||||
| 18 | 24 | ±0,25 | 0,50 | ±0,17 | 0,34 | ±0,12 | 0,24 | ±0,32 | ±0,20 |
| 24 | 30 | ±0,30 | 0,60 | ±0,20 | 0,40 | ±0,14 | 0,28 | ||
| 30 | 40 | ±0,37 | 0,74 | ±0,25 | 0,50 | ±0,17 | 0,34 | ±0,50 | ±0,30 |
| 40 | 50 | ±0,44 | 0,88 | ±0,30 | 0,60 | ±0,20 | 0,40 | ||
| 50 | 65 | ±0,52 | 1,04 | ±0,38 | 0,76 | ±0,23 | 0,46 | ±0,71 | ±0,45 |
| 65 | 80 | ±0,60 | 1,20 | ±0,46 | 0,92 | ±0,27 | 0,54 | ||
| 80 | 100 | ±0,68 | 1,38 | ±0,53 | 1,06 | ±0,30 | 0,60 | ±0,90 | ±0,60 |
| 100 | 120 | ±0,76 | 1,52 | ±0,60 | 1,20 | ±0,33 | 0,66 | ||
| 120 | 140 | ±0,84 | 1,68 | ±0,65 | 1,30 | ±0,36 | 0,72 | ±1,15 | ±0,85 |
| 140 | 160 | ±0,92 | 1,84 | ±0,72 | 1,44 | ±0,38 | 0,76 | ||
| 160 | 180 | ±1,02 | 2,04 | ±0,80 | 1,60 | ±0,42 | 0,84 | ||
| 180 | 200 | ±1,12 | 2,24 | ±0,88 | 1,76 | ±0,43 | 0,86 | ±1,80 | ±1,00 |
| 200 | 225 | ±1,28 | 2,56 | ±0,95 | 1,90 | ±0,47 | 0,94 | ||
| 225 | 250 | ±1,44 | 2,88 | ±1,05 | 2,10 | ±0,51 | 1,02 | ||
| 250 | 280 | ±1,64 | 3,28 | ±1,15 | 2,30 | ±0,56 | 1,12 | ±2,20 | ±1,25 |
| 280 | 315 | ±1,84 | 3,68 | ±1,25 | 2,50 | ±0,63 | 1,26 | ||